A novel conducting composite material has been prepared by using conducting poly(3,4-ethylenedioxythiophene) (PEDOT) and silica network produced by sol-gel process. The doped PEDOT exhibited excellent conductivity and transparency due to the low bandgap in nature, and silica network provided good mechanical properties and adhesion to the surface of silica glass. In order to utilize the advantages of these materials as well as to serve convenient process, the conducting composite of PEDOT and silica was produced by the in-situ sol-gel process of tetraethylorthosilicate. Physical properties were monitored with varying reaction conditions and the excellent conductive coating materials exhibiting 100 S/cm conductivity, 80% transparency, and 9 H pencil hardenss was prepared.

전도성 고분자인 poly(3,4-ethylenedioxythiophene) (PEDOT)과 졸-겔 공정에 의하여 제조한 실리카를 이용하여 새로운 전도성 복합재료를 제조하였다. PEDOT는 밴드갭이 낮아 산화상태에서 높은 전기전도도와 광학적 투명성을 나타내는 장점이 있으며, 실리카는 우수한 경도와 유리와 같은 피착면과의 좋은 접착력을 제공할 수 있다. 이러한 두 가지 물질의 장점을 동시에 이용함과 동시에 간편한 가공공정을 위하여, 본 연구에서는 유기 규소화합물인 tetraethylorthosilicate(TEOS)와 PEDOT 복합재료를 in-situ 졸-겔 공정을 이용하여 제조하였다. 복합재료 제조시에 제조조건에 따른 물성의 변화를 관찰하였으며, 약 100 S/cm 전기전도도와 80% 이상의 투명도 및 9 H의 연필심 경도를 나타내는 우수한 전도성 코팅재료를 개발하였다.

Keywords: conducting composite; PEDOT; TEOS; in-situ sol-gel process